Bending Aluminum Sheet 6061

When you are bending 0 25 in thick 6061 t6 cracking can occur when bending past an external angle of just 86 degrees.

Bending aluminum sheet 6061.

Aluminum minimum bend radii for 90 degree cold forming of sheet and plate. This site should not be used to determine if a. What about the 6061t6 aluminum plate bending 90 degrees compared to the 3000 series and 5000 series. O 0 0 0 1t 1t 1t 1 1 2 t 2t.

The data provided on our website has been vetted to the best of our availabilities. Will 6061t6 aluminum plate will be cracked at 90 degrees. In my 40 plus years in the trade i have bent quite a lot of 6061 t6 aluminum. 1 2 in.

But the question remains the same which alloy is the best product for bending. Aluminum where necessary 5052 h32 may be bent to 1t and 6061 t6 to 1 1 2t. 6061 aluminum sheet plate are ideal for structural framing base plates gussetts aircraft marine and automotive parts etc. From non heat treatable 3003 and 5052 to the heat treatable 2024 6061 and 7075 you have many options from which to choose.

1 32 in. Clinton aluminum offers a variety of products each covering a wide range of applications and processes. To our valued customers. Per the aluminum association inc.

1 16 in. 1 4 in. 1 8 in. The general purpose 6061 aluminum sheet plate is heat treatable resists cracking due to stress and is easy to weld and machine but limited on formability.

This is generalizing as there are ways to bend 6061 but for general bending you use 3003 or 5052 grain direction bend line should go across the grain for the best bend having said that a typical sharp 90 bend on a piece of 1 8 aluminum sheet should be a minimum 1 8 inside radius use either 3003 or 5052 ideally the bend line should go. The 6061 t6 aluminum sheet has stable performance and high hardness is widely used in industry such as trucks buildings ships vehicles furniture machinery moulds etc. Just like all sheet metal aluminum work hardens during the forming process. That is it gets stronger and harder by working bending it.

3 16 in. 3 8 in. When you are forming aluminum if the radius is sharp small in relation to the material thickness you will overwork the material making it harder more brittle and much more likely to fail.